Recovery of vanadium and tungsten from waste selective catalytic reduction catalysts by K2CO3 roasting and water leaching followed by CaCl2 precipitation
Xianghui Liu
Qiaowen Yang
School of Chemical and Environmental Engineering,China University of Mining and Technology,Beijing,Ding No.11 Xueyuan Road,Haidian District,Beijing 100083,China
摘要：Waste selective catalytic reduction (SCR) catalysts are potential environmental hazards.In this study,the recovery of vanadium and tungsten from waste SCR catalysts by K2CO3 roasting and water leaching was investigated.The roasting and leaching conditions were optimized:the leaching efficiencies of vanadium and tungsten were 91.19％ and 85.36％,respectively,when 18 equivalents of K2CO3 were added to perform the roasting at 900 ℃ for 2 h,followed by leaching at 90 ℃ for 1 h.Notably,in the described conditions,the leaching rate of silicon was only 28.55％.Titanates,including K2Ti6O13 and KTisO17,were also produced.Si removal was achieved in 85％ efficiency adjusting the pH to 9.5,and the Si impurity thus isolated was composed of amorphous Si.Tungsten and vanadium were precipitated using CaCl2.At pH 10 and following the addition of 0.10 mol of H2O2 and 16 equivalents of CaCl2,the precipitating efficiencies of tungsten and vanadium were 96.89％ and 99.65％,respectively.The overall yield of tungsten and vanadium was 82.71％and 90.87％,respectively.
机标关键词：
论文发表日期：2021-01-01
在线出版日期：2025-08-15（本平台首次上网日期，不代表文献的发表时间）
页数：10( 727-736 )
英文信息